Bagaj Pwodwi pou Telefòn MIM Pati

Materyèl: 316L
Fòs rupture: Pi gran pase oswa egal a 500 MPa
Fòs sede: Pi gran pase oswa egal a 180 MPa
Dite: Pi gran pase oswa egal a 120 HV10

Voye rechèch

Entwodiksyon pwodwi

Bagaj Pwodwi pou Telefòn MIM Pati
Atik	Materyèl	Pwosesis Pwodiksyon		Sintering Tanperati		Mwazi	Koutim
Bagaj Pwodwi pou Telefòn	17-4	Metal piki bòdi		1350-1500 degre		Pou yo dwe Customized	Wi
Konpozisyon chimik	C: Mwens pase oswa egal a 0.07 Mn: Mwens pase oswa egal a 1.00 Si: Mwens pase oswa egal a 1.00 Cr:15.5 ~ 17.5 Ni:3.0~5.0 P: Mwens pase oswa egal a 0.04 S: Mwens pase oswa egal a 0.03 Cu:3.0~5.0 Nb plis Ta:{{0}}.15~0.45
Materyèl ki disponib	Ba kabòn asye pur, alyaj Titàn (Ti, TC4), alyaj kwiv, alyaj tengstèn, alyaj difisil, alyaj tanperati ki wo (718, 713)
Fini	Presizyon dimansyon		Dansite pwodwi		Tretman Aparans			Pwa ki apwopriye
Brutalizasyon 1-5μm	（±{{0}}.1 pousan -±0.5 pousan ）		92-95 pousan		Refleksyon glas Polisaj elektwolitik			0.03g-400g）
Pwopriyete mekanik	Fòs rupture σb (MPa): ki gen laj nan 480 degre, pi gran pase oswa egal a 1310; ki gen laj nan 550 degre, pi gran pase oswa egal a 1060; ki gen laj nan 580 degre, pi gran pase oswa egal a 1000; ki gen laj nan 620 degre, pi gran pase oswa egal a 930 Fòs sede kondisyonèl σ0.2 (MPa): ki gen laj nan 480 degre , Pi gran pase oswa egal a 1180; ki gen laj nan 550 degre, pi gran pase oswa egal a 1000; ki gen laj 580 degre , Pi gran pase oswa egal a 865; ki gen laj nan 620 degre, pi gran pase oswa egal a 725 Elongasyon δ5 (pousan): aje nan 480 degre, pi gran pase oswa egal a 10; aje nan 550 degre, pi gran pase oswa egal a 12; aje nan 580 degre, pi gran pase oswa egal a 13; aje nan 620 degre, pi gran pase oswa egal a 16 Rediksyon nan zòn ψ (pousan): aje nan 480 degre, pi gran pase oswa egal a 40; aje nan 550 degre, pi gran pase oswa egal a 45; aje nan 580 degre, pi gran pase oswa egal a 45; aje nan 620 degre, pi gran pase oswa egal a 50 Dite: solisyon solid, mwens pase oswa egal a 363HB ak mwens pase oswa egal a 38HRC; 480 degre aje, pi gran pase oswa egal a 375HB ak pi gran pase oswa egal a 40HRC; 550 degre aje, pi gran pase oswa egal a 331HB ak pi gran pase oswa egal a 35HRC; 580 degre aje, pi gran pase oswa egal a 302HB ak pi gran pase oswa egal a 31HRC; 620 degre aje, pi gran pase oswa egal a 277HB ak pi gran pase oswa egal a 28HRC

Non pwodwi: Bagaj Pwodwi pou Telefòn MIM Pati
Materyèl: 316L
Fòs rupture: Pi gran pase oswa egal a 500 MPa
Fòs sede: Pi gran pase oswa egal a 180 MPa
Dite: Pi gran pase oswa egal a 120 HV10
Dansite: Pi gran pase oswa egal a 7.80?g/cm3
Pwosesis: metal poud piki bòdi, MIM, metaliji poud
Aplikasyon: sak mak

Metal Powder Piki lis materyèl bòdi

Materyèl	Dansite	Dite	Entansite	Elongasyon
316L	7.8	HV180	530	40
17-4PH Eta Sinter	7.7	HRC28	850	7
17-4PH Eta tretman chalè	7.7	HRC40	1100	5
304	7.75	HRB60	500	70
410	7.6	HRC45	900	7
420	7.6	HRC53	900	6
440C	7.6	HRC62	950	5
HK30(310S) chalè ki reziste asye	7.9	HRC30

Tablo presizyon dimansyon pou piki metal poud bòdi
Kondisyon tolerans espesyal yo ka reyalize pa pwosesis segondè, tankou: CNC, tour, machin fraisage, elatriye.

Gwosè	Jeneral MIM Enterprise Manufacturing Tolerances	Anjeneral
{{0}mm	plis /-0.05	plis /-0.05
{{0}mm	plis /-0.10	plis /-0.07
{{0}mm	plis /-0.15	plis /-0.10
{{0}mm	plis /-0.20	plis /-0.15
Karakteristik	Ranje jeneral
Gwosè pati	0.2-50g
Epesè miray la	0.5mm oswa plis

Qinhuangdao Zhongwei Precision Machine Parts Co, Ltd se yon antrepriz dènye kri ki konsantre sou teknoloji poud metal piki, ki espesyalize nan pwodiksyon an nan MIM (metal poud piki bòdi). Konpayi paran li te etabli an 1997 e kounye a gen yon sistèm jesyon, pwodiksyon ak sèvis ki gen matirite. . Avèk filozofi biznis "pote pi gwo valè nan kliyan", konpayi an montre kliyan pwodwi-wo kalite nou yo ak sèvis cho, epi li bay pwodwi navèt MIM, kadna kabinè, gon, manch, Pwodwi pou Telefòn ak lòt seri de pwodwi pati MIM pou ede itilizatè yo. reyalize demann kliyan an pou kliyan an (mache) pote amelyorasyon an jeneral nan bon jan kalite itilizatè a, pou itilizatè a ka jwenn benefis ekonomik ak sosyal nan men li; an menm tan an, kòm yon antrepriz dènye kri ki nan etap devlopman an sante, nou bay anplwaye yo Kontinyèlman jenere revni ak amelyore lavi pwòp tèt ou ak platfòm travay!